Study of microstructure and magnetic properties of L10 FePt/SiO2 thin films
Department of Materials Science, INN, NCSR Demokritos, 153 10 Aghia Paraskevi Attikis, Athens, Greece
a Corresponding author: firstname.lastname@example.org
Published online: 3 July 2014
Achieving magnetic recording densities in excess of 1Tbit/in2 requires not only perpendicular media with anisotropies larger than 7 MJ/m3, making FePt alloys an ideal choice, but also a narrow distribution below 10 nm for a reduced S/N ratio. Such grain size reduction and shape control are crucial parameters for high density magnetic recording, along with high thermal stability. Previous work has shown that the L10 FePt grain size can be controlled by alloying FePt with materials such as C, Ag, and insulators such as AlOx, MgO. Au and Al2O3 also act to segregate and magnetically decouple the FePt grains. Better results were obtained with C with respect to the uniformity of grains and SiO2 with respect to the shape. We present our results on co-sputtering FePt with C or SiO2 (up to 30 vol %) on MgO (001) single crystal substrates at 350 and 500 oC. With C or SiO2 addition we achieved grain size reduction, shape control and isolated structure formation, producing continuous films with high uniformity and a narrow grain size distribution. These additions thus allow us to simultaneously control the coercivity and the S/N ratio. We also will report structural and microstructural properties.
© Owned by the authors, published by EDP Sciences, 2014
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 2.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.