Test of Fibre Bragg Gratings samples under High Fast Neutrons Fluence
Den – Service d’Etudes Analytiques et de Réactivité des Surfaces (SEARS), CEA, Université Paris-Saclay, F-91191, Gif sur Yvette, France 33(0)1.69.08.62.71 firstname.lastname@example.org, email@example.com
SCK•CEN - Belgian Nuclear Research center, Boeretang 200 2400 Mol Belgium firstname.lastname@example.org
Electromagnetism and Telecommunications Department of the University of Mons, 31 Boulevard Dolez, 7000 Mons, Belgium email@example.com
Technological Research Division (TRD) of the French Alternative Energies and Atomic Energy Commission. F-91191, Gif sur Yvette, France firstname.lastname@example.org; email@example.com
Université de Saint-Etienne, Laboratoire Hubert Curien, UMR CNRS 5516, 18, rue du Pr. Lauras, F-42000 Saint-Etienne, France firstname.lastname@example.org; email@example.com; firstname.lastname@example.org
Published online: 10 January 2018
Optical fibre sensors (OFS) are worthy of interest for measurements in nuclear reactor thanks to their unique features, particularly compact size and remote multi-point sensing for some of them. But besides non negligible constraints associated with the high temperature environment of the experiments of interest, it is well known that the performances of OFS can be severely affected by high level of radiations. The Radiation Induced Attenuation (RIA) in the fibre is probably most known effect, which can be to some extent circumvented by using rad hard fibres to limit the dynamic loss. However, when the fast neutron fluence reaches 1018 to 1019 n/cm2, the density and index variations associated to structural changes may deteriorate drastically the performances of OFS even if they are based on rad hard fibres, by causing direct errors in the measurements of temperature and/or strain changes. The aim of the present study is to access the effect of nuclear radiations on the Fabry Perot (FP) and of Fibre Bragg Grating (FBG) sensors through the comparison of measurements made on these OFS - or part of them - before and after irradiation .
In the context of development of OFS for high irradiation environment and especially for Material Testing Reactors (MTRs), Sake 2 experiment consists in an irradiation campaign at high level of gamma and neutron fluxes conducted on samples of fibre optics – bare or functionalised with FBG. The irradiation was performed at two levels of fast neutron fluence: 1 and 3.1019 n/cm2 (E>1MeV), at 250°± 25°C, in the SCK•CEN BR2 reactor (Mol Belgium). An irradiation capsule was designed to allow irradiation at the specified temperature without active control. The neutron fluence was measured with activation dosimeters and the results were compared with MCPN computations. Investigation of bare samples gives information on the density changes, while for the FBGs both density and refractive index perturbation are involved. Some results for bare fibres were reported recently. In this paper, we will focus on the measurements made on FBGs that have been manufactured by different laboratories on SMF 28 fibers: CEA, University of St-Etienne and University of Mons. Tested gratings have been written using various conditions (type of fibre, of laser, writing wavelength, power density, post writing thermal annealing,…), leading to various behaviours after Sake 2 irradiation. Bragg wavelength and reflectivity have been measured before and after irradiation thanks to a special mounting at the same temperature. It appears that a change in the shape after irradiation of the Bragg peak disturb the retrieval of the Bragg wavelength.
The measurements show that for nearly all gratings the Bragg peak remains visible after the irradiation, and that Radiation Induced Bragg Wavelength Shifts (RI-BWSs) vary from few pm (equivalent to an error of less than 1°C for a temperature sensor) to nearly 1 nm (equivalent to 100°C) depending of the FBG types. High RI-BWSs could indeed be expected when considering the huge refractive index variation and compaction of the bare fibre samples that have been measured by other techniques. Post writing thermal annealing is confirmed as a key parameter in order to obtain a more radiation tolerant FBG. Our results show that specific annealing regimes allow making FGBs suitable to perform temperature measurements in a MTR experiment.
Key words: Fiber Bragg Gratting / optical fiber sensors / radiation effect / optical fibres / neutron / gamma / compaction
© The Authors, published by EDP Sciences, 2018
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. (http://creativecommons.org/licenses/by/4.0/).
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.