Effects of elevated temperature on a tungsten alloy at high strain-rate
DynaMat SUPSI Laboratory, University of Applied Sciences and Arts of Southern Switzerland, Via Catenazzi 23, 6850 Mendrisio, Switzerland.
* e-mail: firstname.lastname@example.org
Published online: 9 September 2021
The effects of elevated temperature at high strain rate of a commercial tungsten alloy were investigated. The tests were carried-out at high strainrate (from 850 to 2200 1/s) by means of a Split Hopkinson Tension Bar device on round specimens having diameter and gauge length of 2mm and 5 mm, respectively. The thermal conditions were obtained by means of a water-cooled induction heating system on the specimen mounted on the SHTB. The dependence of ultimate tensile strength on temperature was found to decrease, while the failure strain increased with temperature. The strain rate linearly growths with the temperature.
© The Authors, published by EDP Sciences, 2021
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.