Plastic behaviour and forming limit during biaxial compressions of magnesium alloy AZ31 at room temperature
Graduate School of Natural Science and Technology, Okayama
Tsushima-naka, Kita-ku, Okayama
a e-mail : firstname.lastname@example.org
The plastic behaviour and compressive fracture of AZ31 magnesium alloy were examined at room temperature. The uniaxial compression tests and biaxial compression tests along linear and nonlinear strain paths were carried out until fracture using a unique biaxial compression testing machine developed by author. The results revealed the evolution of plastic anisotropy in biaxial compressions, that is the strain path dependency of work hardening. The adaptability of several forming limit criteria to the compressive fracture of AZ31 alloy was discussed. It was found that the uniform estimation of compressive forming limits by uniaxial and biaxial compressions was difficult by Freudenthal criterion and Oyane criterion. The result of Tresca energy criterion suggested that the criterion based on shear stress has possibility to predict the compressive forming limits at room temperature of AZ31 alloy.
© Owned by the authors, published by EDP Sciences, 2010
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.