Mechanical Testing of Iron based Bulk Metallic Glasses and Their Suitability for Force Sensors
Faculty of Materials Science and Engineering, Warsaw University of Technology, ul. Wołoska 141, 02-507 Warsaw, Poland
a e-mail: email@example.com
Thermal, mechanical and magnetic properties of (Fe-Co)-(Zr/Si)-Nb-B alloys in the form of rapidly quenched rods of 1.2 mm in diameter were studied. The as-cast alloys with Zr were crystalline, and the alloys with Si were amorphous. Microhardness measured at 50 g load is from 500 to 2000 HV (the less cobalt, the higher), and the compressive strength reaches nearly 4000 MPa for Si doped alloys and 2000 MPa for Zr doped ones. This substantial difference may be attributed to partial crystallinity of the latter alloys. The magnetic hysteresis loops of fully amorphous rods measured under compression, exhibited a clear dependence of permeability vs. stress, proving that iron-based bulk metallic glasses may be promising materials for magnetoelastic force sensors.
© Owned by the authors, published by EDP Sciences, 2013
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.